The progress on the surface treatments of metal bipolar plate for Proton exchange fuel cells in DICP
Hou M(侯明)
会议名称International Symposium on Electrochemistry for Energy Conversion and Storage
会议日期2009-8-22
2009-08-22
会议地点中国
页码21/1
部门归属三室
主办者武汉大学
英文摘要Bipolar plate is a key component in proton exchange membrane fuel cells (PEMFCs). It functions as the current conductor between cells, provides the manifold for reactant gases flow, and constitutes the backbone of a fuel cell stack. The requirements for bipolar plates should be high corrosion resistance and electrical conductivity in the harsh environment of PEMFC. Low Cost is also the demand for the commercialization targets of DOE[1]. Metal bipolar plates are the hot topic and extensively researched currently[2]. However, pinhole-free coating on metal bipolar plate with well contacting electrical conductivity is still a big challenge in PEMFC application. Some research activities on metal bipolar plate have been conducted in our lab. 1.Ag-PTFE composite coating[3] Ag–PTFE film was electrodeposited with silver-gilt solution of nicotinic acid by a bi-pulse electroplating power supply on 316 L stainless steel bipolar plate of PEMFC. Results showed that the Ag–PTFE composite coating obviously reduced the defects, enhanced the surface energy on compared with those on the pure Ag. In addition, the interfacial contact resistance of the composite coating stays as low as the pure Ag coating measured by potentiodynamic and potentiostatic tests. A short stack with the bipolar plates was evaluated. 2.CrxNY[4] [5] Pulsed bias arc ion plating was applied in Cr-N coating on 316L stainless steel. Surface micrograph, film thickness, film composition, corrosion resistance, interfacial conductivity and contact angle with water of the sample obtained at the optimal flow rate of N2 were investigated. The atomic ratio of Cr to N was close to 2:1 and the CrN phase with crystal planes of (111), (200), (220) and (311) was found in the film. Potentiodynamic and potentiostatic tests showed that the corrosion resistance of the bipolar plate sample was greatly enhanced. 3.CrC[6] Carbon-based films on 316L stainless steel were prepared by pulsed bias arc ion plating. Three kinds of films were formed including the pure C film, the C–Cr composite film and the C–Cr–N composite film. Interfacial conductivity of the bipolar plate with C–Cr film was the highest, which showed great potential of application. Corrosion tests in simulated PEMFC environments revealed that the C–Cr film coated sample always showed better anticorrosive performance than 316L stainless steel either in reducing or oxidizing environments.
语种中文
文献类型会议论文
条目标识符http://cas-ir.dicp.ac.cn/handle/321008/113786
专题中国科学院大连化学物理研究所
通讯作者Hou M(侯明)
推荐引用方式
GB/T 7714
Hou M. The progress on the surface treatments of metal bipolar plate for Proton exchange fuel cells in DICP[C],2009:21/1.
条目包含的文件
条目无相关文件。
个性服务
推荐该条目
保存到收藏夹
查看访问统计
导出为Endnote文件
谷歌学术
谷歌学术中相似的文章
[侯明]的文章
百度学术
百度学术中相似的文章
[侯明]的文章
必应学术
必应学术中相似的文章
[侯明]的文章
相关权益政策
暂无数据
收藏/分享
所有评论 (0)
暂无评论
 

除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。