New methods to prepare perovskite-type La0.8Sr0.2CoO3 catalyst at low temperature
Shao, ZP; Xiong, GX; Sheng, SS; Chen, HR; Li, L; Delmon, B; Jacobs, PA; Maggi, R; Martens, JA; Grange, P; Poncelet, G
Source PublicationPREPARATION OF CATALYSTS VII
1998
Volume118Pages:431-439
Indexed ByISTP ; SCI
SubtypeArticle
WOS HeadingsScience & Technology ; Physical Sciences
WOS SubjectChemistry, Physical
WOS Research AreaChemistry
WOS KeywordOXYGEN PERMEATION ; OXIDES ; DECOMPOSITION
AbstractA pure phase perovskite-type composite oxide La0.8Sr0.2CoO3 (LSCO) was prepared by three methods: sol-gel method using EDTA as ligand, environmentaly safe metal-EDTA-cellulose complexing method and metal-citric-cellulose complexing method. The formation processes of LSCO by those methods were investigated by TG-DTA, XRD and IR spectroscopy. The results indicated that when EDTA complexing method was used, at optimized condition, pure phase perovskite-type LSCO was acquired after the precursor was fired at 800 degrees C for 2hr. In the process of forming perovskite LSCO, SrCO3 was formed and calcination temperatures higher than 800 degrees C was needed to get rid of it, similar to the citric complexing method reported. When cellulose was introduced, the minimum calcination temperature to acquire pure phase LSCO was significantly lowered to around 600 degrees C for metal-EDTA-cellulose method and 540 degrees C for metal-citric-cellulose method. Low calcination temperature led to relatively high BET area for 21m(2)/g and 22m(2)/g respectively. But the surface area were significantly reduced to 12.7m(2)/g and 12.1m(2)/g respectively when they were further fired at 620 degrees C for 2hr.
Language英语
WOS IDWOS:000076264000047
Citation statistics
Cited Times:15[WOS]   [WOS Record]     [Related Records in WOS]
Document Type期刊论文
Identifierhttp://cas-ir.dicp.ac.cn/handle/321008/138135
Collection中国科学院大连化学物理研究所
AffiliationChinese Acad Sci, Dalian Inst Chem Phys, State Key Lab Catalysis, Dalian 116023, Peoples R China
Recommended Citation
GB/T 7714
Shao, ZP,Xiong, GX,Sheng, SS,et al. New methods to prepare perovskite-type La0.8Sr0.2CoO3 catalyst at low temperature[J]. PREPARATION OF CATALYSTS VII,1998,118:431-439.
APA Shao, ZP.,Xiong, GX.,Sheng, SS.,Chen, HR.,Li, L.,...&Poncelet, G.(1998).New methods to prepare perovskite-type La0.8Sr0.2CoO3 catalyst at low temperature.PREPARATION OF CATALYSTS VII,118,431-439.
MLA Shao, ZP,et al."New methods to prepare perovskite-type La0.8Sr0.2CoO3 catalyst at low temperature".PREPARATION OF CATALYSTS VII 118(1998):431-439.
Files in This Item:
There are no files associated with this item.
Related Services
Recommend this item
Bookmark
Usage statistics
Export to Endnote
Google Scholar
Similar articles in Google Scholar
[Shao, ZP]'s Articles
[Xiong, GX]'s Articles
[Sheng, SS]'s Articles
Baidu academic
Similar articles in Baidu academic
[Shao, ZP]'s Articles
[Xiong, GX]'s Articles
[Sheng, SS]'s Articles
Bing Scholar
Similar articles in Bing Scholar
[Shao, ZP]'s Articles
[Xiong, GX]'s Articles
[Sheng, SS]'s Articles
Terms of Use
No data!
Social Bookmark/Share
All comments (0)
No comment.
 

Items in the repository are protected by copyright, with all rights reserved, unless otherwise indicated.