Improved cellulose adsorption method for the preparation of perovskite oxides with large specific surface area at low temperature
Shao, ZP; Li, GT; Xiong, GX; Yang, WS
关键词Perovskite Synthesis Cellulose Organic Acid Surface Area
刊名CHINESE CHEMICAL LETTERS
2000-12-01
11期:12页:1103-1106
收录类别SCI
文章类型Article
WOS标题词Science & Technology ; Physical Sciences
类目[WOS]Chemistry, Multidisciplinary
研究领域[WOS]Chemistry
英文摘要Perovskite-type La1-xSrxMO3-delta (x=0,0.1,0.2, B=Co,Fe,Mn) oxides were prepared by pyrolysis of metal salt-(organic acid)-cellulose compound precursors. Low calcination temperatures, usually lower than 600 degreesC, were needed. The specific surface area of the as-prepared oxides is higher than that prepared by the cellulose adsorption method, and is comparable to that prepared by sol-gel method. The effective organic acid could be EDTA acid, citric acid or DL-hydroxysuccinic acid, among them, EDTA acid is the best one.
语种英语
WOS记录号WOS:000165960400021
引用统计
文献类型期刊论文
条目标识符http://cas-ir.dicp.ac.cn/handle/321008/138734
专题中国科学院大连化学物理研究所
作者单位Chinese Acad Sci, Dalian Inst Chem Phys, State Key Lab Catalysis, Dalian 116023, Peoples R China
推荐引用方式
GB/T 7714
Shao, ZP,Li, GT,Xiong, GX,et al. Improved cellulose adsorption method for the preparation of perovskite oxides with large specific surface area at low temperature[J]. CHINESE CHEMICAL LETTERS,2000,11(12):1103-1106.
APA Shao, ZP,Li, GT,Xiong, GX,&Yang, WS.(2000).Improved cellulose adsorption method for the preparation of perovskite oxides with large specific surface area at low temperature.CHINESE CHEMICAL LETTERS,11(12),1103-1106.
MLA Shao, ZP,et al."Improved cellulose adsorption method for the preparation of perovskite oxides with large specific surface area at low temperature".CHINESE CHEMICAL LETTERS 11.12(2000):1103-1106.
条目包含的文件
条目无相关文件。
个性服务
推荐该条目
保存到收藏夹
查看访问统计
导出为Endnote文件
谷歌学术
谷歌学术中相似的文章
[Shao, ZP]的文章
[Li, GT]的文章
[Xiong, GX]的文章
百度学术
百度学术中相似的文章
[Shao, ZP]的文章
[Li, GT]的文章
[Xiong, GX]的文章
必应学术
必应学术中相似的文章
[Shao, ZP]的文章
[Li, GT]的文章
[Xiong, GX]的文章
相关权益政策
暂无数据
收藏/分享
所有评论 (0)
暂无评论
 

除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。