Investigation of the permeation behavior and stability of a Ba0.5Sr0.5Co0.8Fe0.2O3-delta oxygen membrane
Shao, ZP; Yang, WS; Cong, Y; Dong, H; Tong, JH; Xiong, GX
关键词Inorganic Membrane Ba0.5sr0.5co0.8fe0.2o3-delta Perovskite Oxygen Separation Phase Stability
刊名JOURNAL OF MEMBRANE SCIENCE
2000-07-01
172期:1-2页:177-188
收录类别SCI
文章类型Article
WOS标题词Science & Technology ; Technology ; Physical Sciences
类目[WOS]Engineering, Chemical ; Polymer Science
研究领域[WOS]Engineering ; Polymer Science
关键词[WOS]MIXED-CONDUCTING OXIDES ; PARTIAL OXIDATION ; METHANE ; REACTORS ; SYNGAS ; GAS ; SRCO0.8FE0.2O3-DELTA ; PERMEABILITY ; PEROVSKITES ; CONVERSION
英文摘要SrCo0.8Fe0.2O3-delta (SCFO) and Ba0.5Sr0.5Co0.8Fe0.2O3-delta (BSCFO) oxides were successfully prepared, using a combined citrate-EDTA complexing method. The results of O-2-TPD and XRD showed that the introduction of barium into SCFO could effectively suppress the oxidation of Co3+ and Fe3+ to higher valence states of Co4+ and Fe4+ in the lattice, and stabilize the perovskite structure under lower oxygen partial pressures. Oxygen permeation experiment showed that BSCFO membrane also had higher oxygen permeation flux than that of SCFO under air/He oxygen partial pressure gradient. At 950 degrees C, the permeation flux through 1.80 mm BSCFO membrane exposed to flowing predried air (P-O2' = 0.21 atm) and helium (P-O2" = 0.037 atm) is ca. 1.4 ml/cm(2) min and the activation energy for oxygen transportation is 40.9 kJ/mol within the temperature range of 775-950 degrees C. The permeation flux of BSCFO was less sensitive to minor amounts of CO2 and water vapor presented in the air than that of SCFO. Long-term oxygen permeation study of more than 1000 h at 850 degrees C indicated that the BSCFO membrane could operate stably as an oxygen generator at that temperature. A very slow exponential decay in the measured oxygen permeation flux occurred at temperatures lower than 825 degrees C, which was caused by a phase transition. The phase transition was found to be reversible at higher temperatures, but a long time was needed for the equilibration. (C) 2000 Elsevier Science B.V. All rights reserved.
语种英语
WOS记录号WOS:000087289200017
引用统计
文献类型期刊论文
条目标识符http://cas-ir.dicp.ac.cn/handle/321008/138821
专题中国科学院大连化学物理研究所
作者单位Chinese Acad Sci, Dalian Inst Chem Phys, State Key Lab Catalysis, Dalian 116023, Peoples R China
推荐引用方式
GB/T 7714
Shao, ZP,Yang, WS,Cong, Y,et al. Investigation of the permeation behavior and stability of a Ba0.5Sr0.5Co0.8Fe0.2O3-delta oxygen membrane[J]. JOURNAL OF MEMBRANE SCIENCE,2000,172(1-2):177-188.
APA Shao, ZP,Yang, WS,Cong, Y,Dong, H,Tong, JH,&Xiong, GX.(2000).Investigation of the permeation behavior and stability of a Ba0.5Sr0.5Co0.8Fe0.2O3-delta oxygen membrane.JOURNAL OF MEMBRANE SCIENCE,172(1-2),177-188.
MLA Shao, ZP,et al."Investigation of the permeation behavior and stability of a Ba0.5Sr0.5Co0.8Fe0.2O3-delta oxygen membrane".JOURNAL OF MEMBRANE SCIENCE 172.1-2(2000):177-188.
条目包含的文件
条目无相关文件。
个性服务
推荐该条目
保存到收藏夹
查看访问统计
导出为Endnote文件
谷歌学术
谷歌学术中相似的文章
[Shao, ZP]的文章
[Yang, WS]的文章
[Cong, Y]的文章
百度学术
百度学术中相似的文章
[Shao, ZP]的文章
[Yang, WS]的文章
[Cong, Y]的文章
必应学术
必应学术中相似的文章
[Shao, ZP]的文章
[Yang, WS]的文章
[Cong, Y]的文章
相关权益政策
暂无数据
收藏/分享
所有评论 (0)
暂无评论
 

除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。