Crystal structure and oxygen permeation study of cobalt doped Sr4Fe6O13 mixed-conducting oxides
Dong, H; Shao, ZP; Xiong, GX; Yang, WS
关键词Mixed-conducting Oxide Cellulose Sr4coxfe6-o-x(13 +/-delta) Phase Structure Oxygen Separation
刊名JOURNAL OF INORGANIC MATERIALS
2001-03-01
16期:2页:311-318
收录类别SCI
文章类型Article
WOS标题词Science & Technology ; Technology
类目[WOS]Materials Science, Ceramics
研究领域[WOS]Materials Science
关键词[WOS]CERAMIC MEMBRANE ; STABILITY ; METHANE ; SYNGAS
英文摘要Mixed-conducting Sr4CoxFe6-xO13+/-delta oxides were synthesized by pyrolysis of cellulose-citric-metal salt compound. Their crystal structures were investigated, and oxygen permeability of Sr4Co2Fe4O13+/-delta was also studied by a GC method. The introduction of cobalt in Sr4Fe6O13 led to the occurrence of perovskite phase in the Sr4Fe6O13 bulk even at low doping content of cobalt (x=0.5), some minor CoO phase was also observed when x=2.0, and the material mainly demonstrated perovskite structure when x=2.6. The phase structure of Sr4COxFe6-xO13+/-delta was found to be closely related with the calcined temperature and the oxygen concentration in the ambient atmosphere during calcination or retreatment at high temperature. The air-synthesized sample had the intergrowth phase Sr4Fe6-xCoxO13+/-delta and the perovskite phase Sr(Fe, Co)O3-delta coexisted along with CoO impurity. The N-2-annealed sample coexisted of Sr4Fe6O13 phase, brownmillerite phase and minor CoO impuirty. When Sr4Co2Fe4O13+/-delta was treated in pure oxygen environment, the sample changed to single phase (Sr4Fe6O13 type phase). The oxygen permeability of Sr4Co2Fe4O13+/-delta membrane had a value close to 1.5x10(-8)mol/cm(2).s at 1123K. From 923K to 1223K, the activation energy for oxygen transportation was about 70kJ/mol.
语种英语
WOS记录号WOS:000167638500019
引用统计
文献类型期刊论文
条目标识符http://cas-ir.dicp.ac.cn/handle/321008/138970
专题中国科学院大连化学物理研究所
作者单位Chinese Acad Sci, Dalian Inst Chem Phys, State Key Lab Catalysis, Dalian 116023, Peoples R China
推荐引用方式
GB/T 7714
Dong, H,Shao, ZP,Xiong, GX,et al. Crystal structure and oxygen permeation study of cobalt doped Sr4Fe6O13 mixed-conducting oxides[J]. JOURNAL OF INORGANIC MATERIALS,2001,16(2):311-318.
APA Dong, H,Shao, ZP,Xiong, GX,&Yang, WS.(2001).Crystal structure and oxygen permeation study of cobalt doped Sr4Fe6O13 mixed-conducting oxides.JOURNAL OF INORGANIC MATERIALS,16(2),311-318.
MLA Dong, H,et al."Crystal structure and oxygen permeation study of cobalt doped Sr4Fe6O13 mixed-conducting oxides".JOURNAL OF INORGANIC MATERIALS 16.2(2001):311-318.
条目包含的文件
条目无相关文件。
个性服务
推荐该条目
保存到收藏夹
查看访问统计
导出为Endnote文件
谷歌学术
谷歌学术中相似的文章
[Dong, H]的文章
[Shao, ZP]的文章
[Xiong, GX]的文章
百度学术
百度学术中相似的文章
[Dong, H]的文章
[Shao, ZP]的文章
[Xiong, GX]的文章
必应学术
必应学术中相似的文章
[Dong, H]的文章
[Shao, ZP]的文章
[Xiong, GX]的文章
相关权益政策
暂无数据
收藏/分享
所有评论 (0)
暂无评论
 

除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。