题名: Analysis of PEMFC freeze degradation at-20 degrees C after gas purging
作者: Hou, Junbo;  Yu, Hongmei;  Zhang, Shengsheng;  Sun, Shucheng;  Wang, Hongwei;  Yi, Baolian;  Ming, Pingwen
关键词: subzero storage ;  degradation ;  relative humidity ;  proton exchange membrane fuel cell (PEMFC)
刊名: JOURNAL OF POWER SOURCES
发表日期: 2006-11-08
DOI: 10.1016/j.jpowsour.2006.07.010
卷: 162, 期:1, 页:513-520
收录类别: SCI
文章类型: Article
WOS标题词: Science & Technology ;  Physical Sciences ;  Technology
类目[WOS]: Electrochemistry ;  Energy & Fuels
研究领域[WOS]: Electrochemistry ;  Energy & Fuels
英文摘要: Proton exchange membrane fuel cell (PEMFC) freeze degradation was investigated using 20 freeze/thaw cycles of two cells with gases purged immediately after operation. The cell purged by gas with an RH 58.0% at 25 degrees C was found to have no performance loss after the 20 freeze/thaw cycles. From the cell resistances and the electrochemical impedance spectra (EIS), the electrolyte conductivity and interfacial charge transfer resistance were unchanged. The electrochemical active surface area (ECSA) from the cyclic voltammetry (CV) measurements indicated that the amount of water in the catalyst layer of the cell was reduced to an extent that the damage in the freeze/thaw cycles was avoided. Another cell was purged by RH 64.9% gas in the first cycle, and then was purged with RH 45.0% gas in 19 freeze/thaw cycles. Although the cell easily became flooded at high current densities after the first cycle; no further performance loss was found. The pore size distribution data from mercury intrusion porosimetry measurements suggested that the gas diffusion layer was changed by the first freeze cycles. The micrographs (SEM) further proved no membrane electrode assembly (MEA) delamination. These results shed some light on the relationship of the water amount in the cell to subzero temperature exposure. (c) 2006 Elsevier B.V. All rights reserved.
关键词[WOS]: ELECTROLYTE FUEL-CELL ;  PLATINUM LOADING ELECTRODES ;  REPETITIVELY BROUGHT ;  WATER ;  PERFORMANCE ;  IMPEDANCE ;  TRANSPORT ;  MEMBRANES ;  BEHAVIOR ;  SIZE
语种: 英语
WOS记录号: WOS:000242059700062
Citation statistics: 
内容类型: 期刊论文
URI标识: http://cas-ir.dicp.ac.cn/handle/321008/140000
Appears in Collections:中国科学院大连化学物理研究所_期刊论文

Files in This Item:

There are no files associated with this item.


作者单位: 1.Chinese Acad Sci, Dalian Inst Chem Phys, Fuel Cell R&D Ctr, Dalian 116023, Peoples R China
2.Chinese Acad Sci, Grad Sch, Beijing 100039, Peoples R China
3.Beijing Jiaotong Univ, Sch Sci, Beijing 100044, Peoples R China

Recommended Citation:
Hou, Junbo,Yu, Hongmei,Zhang, Shengsheng,et al. Analysis of PEMFC freeze degradation at-20 degrees C after gas purging[J]. JOURNAL OF POWER SOURCES,2006,162(1):513-520.
Service
 Recommend this item
 Sava as my favorate item
 Show this item's statistics
 Export Endnote File
Google Scholar
 Similar articles in Google Scholar
 [Hou, Junbo]'s Articles
 [Yu, Hongmei]'s Articles
 [Zhang, Shengsheng]'s Articles
CSDL cross search
 Similar articles in CSDL Cross Search
 [Hou, Junbo]‘s Articles
 [Yu, Hongmei]‘s Articles
 [Zhang, Shengsheng]‘s Articles
Related Copyright Policies
Null
Social Bookmarking
  Add to CiteULike  Add to Connotea  Add to Del.icio.us  Add to Digg  Add to Reddit 
所有评论 (0)
暂无评论
 
评注功能仅针对注册用户开放,请您登录
您对该条目有什么异议,请填写以下表单,管理员会尽快联系您。
内 容:
Email:  *
单位:
验证码:   刷新
您在IR的使用过程中有什么好的想法或者建议可以反馈给我们。
标 题:
 *
内 容:
Email:  *
验证码:   刷新

Items in IR are protected by copyright, with all rights reserved, unless otherwise indicated.

 

 

Valid XHTML 1.0!
Powered by CSpace