Sintering mechanism of porous matrix for molten carbonate fuel cell
Lin Hua-Xin; Zhou Li; Zhang Hua-Min
关键词Molten Carbonate Fuel Cell Matrix Rearrangement And Slip Maximum Pore Diameter Trapezium Model
刊名JOURNAL OF INORGANIC MATERIALS
2007-07-01
22期:4页:759-764
收录类别SCI
文章类型Article
WOS标题词Science & Technology ; Technology
类目[WOS]Materials Science, Ceramics
研究领域[WOS]Materials Science
英文摘要In initial sintering stage of the porous (porosity >= 50%) matrix impregnated fully with molten carbonate (46wt% electrolyte) and sintered under the cell stacking pressure, the sintering brought about the rearrangements and slips of powder particles by which the maximum pore diameter altered into a smaller one. Its maximum pore diameter and slip rate were smaller and oppositely higher respectively than those in the matrix impregnated with the less (5wt%) electrolyte and sintered under the ordinary pressure. The cell stacking pressure facilitated the rearrangements and slips of powder particles, but effectively suppressed and diminished defect developments in the sintered matrix. Porosity in the matrix increased, micro-pores altered into bigger ones, mean pore diameter increasing and pore-size distribution becoming narrowly with sintering time by the synergetic action of the rearrangements of powder particles and its accompanying mechanisms. As indicated above, the sintering behaviors and the alteration of some physical properties with sintering time in the porous matrix are different from those in traditional ceramics. So the rearrangement of powder particles dominates over the sintering mechanisms of the porous matrix, its sintering model conforms to the trapezium model.
语种英语
WOS记录号WOS:000248928700038
引用统计
被引频次:1[WOS]   [WOS记录]     [WOS相关记录]
文献类型期刊论文
条目标识符http://cas-ir.dicp.ac.cn/handle/321008/140529
专题中国科学院大连化学物理研究所
作者单位Chinese Acad Sci, Dalian Inst Chem Phys, Dalian 116023, Peoples R China
推荐引用方式
GB/T 7714
Lin Hua-Xin,Zhou Li,Zhang Hua-Min. Sintering mechanism of porous matrix for molten carbonate fuel cell[J]. JOURNAL OF INORGANIC MATERIALS,2007,22(4):759-764.
APA Lin Hua-Xin,Zhou Li,&Zhang Hua-Min.(2007).Sintering mechanism of porous matrix for molten carbonate fuel cell.JOURNAL OF INORGANIC MATERIALS,22(4),759-764.
MLA Lin Hua-Xin,et al."Sintering mechanism of porous matrix for molten carbonate fuel cell".JOURNAL OF INORGANIC MATERIALS 22.4(2007):759-764.
条目包含的文件
条目无相关文件。
个性服务
推荐该条目
保存到收藏夹
查看访问统计
导出为Endnote文件
谷歌学术
谷歌学术中相似的文章
[Lin Hua-Xin]的文章
[Zhou Li]的文章
[Zhang Hua-Min]的文章
百度学术
百度学术中相似的文章
[Lin Hua-Xin]的文章
[Zhou Li]的文章
[Zhang Hua-Min]的文章
必应学术
必应学术中相似的文章
[Lin Hua-Xin]的文章
[Zhou Li]的文章
[Zhang Hua-Min]的文章
相关权益政策
暂无数据
收藏/分享
所有评论 (0)
暂无评论
 

除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。