Chloride flux growth of crystalline strontium niobates and nitridation to perovskite SrNbO2N
Li, Yue1,2; Xiong, Feng-Qiang2; Ou, Ruiling1,2; Wan, Lipeng1,2; Yin, Congling3; Che, Ruxin1; Yang, Minghui2
KeywordPerovskites Niobates Strontium Niobium Oxynitride Defects
Source PublicationCERAMICS INTERNATIONAL
2017-07-01
DOI10.1016/j.ceramint.2017.03.071
Volume43Pages:7695-7700
Indexed BySCI
SubtypeArticle
WOS HeadingsScience & Technology ; Technology
WOS SubjectMaterials Science, Ceramics
WOS Research AreaMaterials Science
WOS KeywordVISIBLE-LIGHT IRRADIATION ; MOLTEN-SALT SYNTHESIS ; DIELECTRIC-PROPERTIES ; LATIO2N CRYSTALS ; OXYNITRIDE ; OXIDE ; PARTICLES ; SR2NB2O7 ; SR4NB2O9 ; SR
AbstractHighly crystalline (110) layered perovskite Sr2Nb2O7, (111) layered perovskite Sr5Nb4O15 and complex perovskite Sr4Nb2O9 were prepared by NaCl-KCl flux growth method from SrCO3 and Nb2O5. This flux synthesis achieves single strontium niobate phase in contrast to mixed niobates from the solid state reaction with the same heating parameters. A little excess of Sr source was found to be required for the synthesis of Sr5Nb4O15 and Sr4Nb2O9 at elevated temperature due to slight evaporation. The three strontium niobates were converted to perovskite SrNbO2N via thermal ammonolysis under NH3 flow at 900 degrees C. Post-wash treatment was performed to remove the byproduct SrO. This makes additional nanopores in SrNbO2N in the cases of Sr5Nb4O15 and Sr4Nb2O9, and results in increasing surface areas of SrNbO2N with Sr:Nb ratios in the precursors (from 9.9 to 19.8 and 35.5 m(2)/g). On the other hand, the UV Vis diffusion reflectance spectra reveal decreasing light absorption by defects in SrNbO2N in this order. This suggests fewer low-valent Nb defects in SrNbO2N prepared from precursor with higher Sr:Nb ratio. SrNbO2N prepared from Sr4Nb2O9 would be advantageous for applications that require high surface area and low defect density of the material.
Language英语
WOS IDWOS:000400880000045
Citation statistics
Document Type期刊论文
Identifierhttp://cas-ir.dicp.ac.cn/handle/321008/152313
Collection中国科学院大连化学物理研究所
Affiliation1.Dalian Jiaotong Univ, Coll Environm & Chem Engn, Coll Mat Sci & Engn, Dalian 116028, Peoples R China
2.Chinese Acad Sci, Dalian Inst Chem Phys, Dalian Natl Lab Clean Energy, Dalian 116023, Peoples R China
3.Jiangxi Univ Sci & Technol, Sch Mat Sci & Engn, Ganzhou 341000, Peoples R China
Recommended Citation
GB/T 7714
Li, Yue,Xiong, Feng-Qiang,Ou, Ruiling,et al. Chloride flux growth of crystalline strontium niobates and nitridation to perovskite SrNbO2N[J]. CERAMICS INTERNATIONAL,2017,43:7695-7700.
APA Li, Yue.,Xiong, Feng-Qiang.,Ou, Ruiling.,Wan, Lipeng.,Yin, Congling.,...&Yang, Minghui.(2017).Chloride flux growth of crystalline strontium niobates and nitridation to perovskite SrNbO2N.CERAMICS INTERNATIONAL,43,7695-7700.
MLA Li, Yue,et al."Chloride flux growth of crystalline strontium niobates and nitridation to perovskite SrNbO2N".CERAMICS INTERNATIONAL 43(2017):7695-7700.
Files in This Item:
There are no files associated with this item.
Related Services
Recommend this item
Bookmark
Usage statistics
Export to Endnote
Google Scholar
Similar articles in Google Scholar
[Li, Yue]'s Articles
[Xiong, Feng-Qiang]'s Articles
[Ou, Ruiling]'s Articles
Baidu academic
Similar articles in Baidu academic
[Li, Yue]'s Articles
[Xiong, Feng-Qiang]'s Articles
[Ou, Ruiling]'s Articles
Bing Scholar
Similar articles in Bing Scholar
[Li, Yue]'s Articles
[Xiong, Feng-Qiang]'s Articles
[Ou, Ruiling]'s Articles
Terms of Use
No data!
Social Bookmark/Share
All comments (0)
No comment.
 

Items in the repository are protected by copyright, with all rights reserved, unless otherwise indicated.